7075 alloy aluminum bar contains zinc and magnesium and is stronger than common aluminum alloys. However, it cannot be welded and its corrosion resistance is quite poor. Many CNC cut parts are made from 7075 alloys.
7000 aluminum Bar Feature:
1. high strength heat treatable alloy.
2. good mechanical properties.
3. easy to use.
4. easy processing, good resistance to abrasion.
5. good corrosion resistance, oxidation resistance.
7000 aluminum Bar property:
1.σb (MPa)：≥560
2.σp0.2 (MPa)：≥495
3.δ5 (%)：≥6
7000 aluminum Bar Packing & shipment:
Packing: To be packed by standard seaworthy packing or according to your requirement
Shipment: About 25 days after received your advance
7000 aluminum Bar Applications:
Storage device, decoration, pressure vessels ,Aerospace industry, blowing (bottle) dies, ultrasonic plastic welding mold, golf heads, shoes, paper mold, foam molding, de la mode equipment, tooling, temBars, jigs, machinery processing, used to produce high-end aluminum bike frame.
7075 Aluminum bar Specifications
Aluminum Alloy: 7075
Alloy Designations: AA7075, A7075, 7075A
Temper: T6, T651, T7351, O
Hardness: above 150HB
Standard: GB/T 3880-2012, ASTM B209,
Diameter: Φ10-90*3000MM, Φ90-190*2000MM, Φ190-310*1000MM,Φ310-700*1000MM
Aluminum round bar: Φ4mm-410mm
Aluminum square bar 7075 T651
Aluminum bar stock quantity: over 1,500 Tons
7075 T6 Aluminum bar Chemistry Composition / 7075-T6 Date Sheet:
| ALLOY | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | A1 | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 7075 | 0.4 | 0.5 | 1.2~2.0 | 0.3 | 2.1~2.9 | 0.18~0.28 | — | 5.1~6.1 | — | 0.2 | — | Remainder |
7075 T651 Aluminum bar Mechanical Properties / Properties of alloy 7075-T651:
| Temper | Anti –tensile strength N/m㎡ | Elongation rate（%） | surface | Hardness |
|---|---|---|---|---|
| 7075 T6 | 580Mpa | 11 | Black / Bright | Above 160HB |
| 7075 T651 | 595Mpa | 14 | Black / Bright | Above 160HB |
7075 T651 Aluminum bar Physical Propertie
| Aluminum bar | (20-100℃) μm/m·k Rm/Mpa | (℃) Rp0.2/Mpa | 20℃(68℉) (%IACS) | 20℃(68℉) Ωmm2/m | (20℃)(g/cm3) Ωmm2/m |
|---|---|---|---|---|---|
| 7075-T6 | 23.5 | 475-635 | 33 | 0.0515 | 2.8 |
High strength heat treatable alloy.
Good mechanical properties.
Good serviceability.
Easy processing, good wear resistance.
Good corrosion resistance and oxidation resistance.
T7351 state enhanced corrosion resistance fracture
High strength material for high-pressure structural parts.