The main alloying elements of the 6061 aluminum bar are magnesium and silicon, which have medium strength, good corrosion resistance, and a good oxidation effect. After the T6 heat treatment, the 6061 aluminum alloy bar is widely used in automatic mechanical parts, precision machining, and various mold manufacturing.
Specifications aluminum Bar 6000 series
alloy:6061 6063 6082 6A02 etc.
temper:O-H112
size:thickness:0.5-8mm, width:600-1250mm,Length:3-12m
Mill finished
Anodize: silver, champagne, light bronze, dark bronze, black, light titanium, dark titanium.
Electrophoretic coated: silver, champagne, bronze, black, light bronze, dark bronze.
Powder spray coated: normal color, special color.
Fluorocarbon powder spray coated: normal color, special color.
Acrylic paint coated: normal color, special color.
Wood grain coated: import paper, domestic paper.
Features of 6061 Series Aluminum Bar
It is a kind of aluminum Bar which can be forged with cold treatment. It can be used in situations which have high demand in anti-corrosion and oxidation.
As a result of its good availability and its connector with super features, it is easily coated and has good processability.
Aluminum Alloy: 6061
Alloy Designations: A6061, 6061-T6, 6061-T651
Temper: T6, T651, T7351, O
Hardness: above 95HB
Standard: GB/T 3880-2012, ASTM B209,
Diameter: Φ10-90*3000MM, Φ90-190*2000MM, Φ190-310*1000MM,Φ310-700*1000MM
Aluminum round bar: Φ10mm-600mm
Aluminum square bar 6061-T6
6061 T6 Aluminum bar Chemistry Composition / 6061-T651 bar Date Sheet:
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | A1 | ||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 6061 | 0.40~0.8 | 0.7 | 0.15~0.40 | 0.15 | 0.8~1.2 | 0.04~0.35 | — | 0.25 | — | 0.15 | — | Remainder | |
6061 T651 Aluminum bar Mechanical Properties / Properties of alloy 6061-T651 bar:
| Temper | Anti –tensile strength N/m㎡ | Elongation rate（%） | Dimension Control | Surface | Hardness |
|---|---|---|---|---|---|
| 6061 T6 | 290Mpa | 10 | Qualified | Black / Bright | Above 95HB |
| 6061 T651 | 290Mpa | 10 | Qualified | Black / Bright | Above 95HB |
6061 Aluminum bar Physical Properties
| Aluminum bar | (20-100℃) μm/m·k Rm/Mpa | (℃) Rp0.2/Mpa | 20℃(68℉) (%IACS) | 20℃(68℉) Ωmm2/m | (20℃)(g/cm3) Ωmm2/m |
|---|---|---|---|---|---|
| 6061 T6 | 23.6 | 582-652 | 40 | 0.043 | 2.8 |
Aluminum alloy bar 6061 Characteristics:
high corrosion resistance
welding and anodizing
Heat treatment, hardness over 95HB
The Max diameter we can produce is 600mm