The combination of magnesium and silicon in 6061 aluminum allows it to be heat treated to higher strength levels. It has good formability when in the fully soft, annealed condition and the strength can be significantly increased following a heat treatment.
Alloy: 6061
Temper: O / T4 / T6 / T651 / T351 / T5
Produce to ASTM B209 or GB/T3880, EN485 standard;
Standard size: 4 x 8; 1219 x 2438mm, 1250 x 2500mm, 1500mm x 3000mm;
Surface: mill finish, unpolished, polished, black surface, bright surface,
6000 Series Alloy (Generally called Al-Mg-Si Alloy, the Mg and Si are used as main alloy elements ) | |
Alloy | 6061 6063 6082 |
Temper | O F, etc. |
Specification | Thickness≤170mm; Width≤2200mm ; Length≤12000mm |
Application | Automotive, Aluminium For Aviation, Industrial Mould, Mechanical Components, |
Feature | Good corrosion resistant performance, well welding property, good oxidability, |
| Temper | Anti –tensile strength N/m㎡ | Elongation rate（%） | Dimension Control | Surface | Hardness |
| 6061 T6 | 290Mpa | 10 | Qualified | Black / Bright | Above 95HB |
| 6061 T651 | 290Mpa | 10 | Qualified | Black / Bright | Above 95HB |